Supply German Baolong IMD / IML ink NoriPET series, Germany Baolong IMD / IML / FIM Series ink NoriPET two-component screen printing inks are solvent-based inks, dedicated to the back of the printed PET film in the IMD / FIM product or a membrane switch products. Forming and pressure forming machines can be. Forming depth depends on the PET sheet. 

 Printed on the PET sheet material, such as Autoflex EBG 180 L and Autotex V 200 is used on the following characteristics: 
 Good formability and stretchability 
 When the temperature of the injection molding process 
 On the film and resins such as ABS plastic with good adhesive layer adhesion is not printed 

 Shiny gloss of printed materials by 
 Does not contain toxic heavy metals NoriPET color pigments (in accordance with DIN EN 71, part 3). 
 Polyester mesh screen is recommended 90-150 T / cm (ie 230 380 T / inch) 
 Stencil-type photosensitive emulsion solvent must be used. 


 Additives 
 Catalyst Catalyst Catalyst NoriPET 005, should be added before printing inks, it is necessary to fully uniform mixing. Dosage: 13%. And hardener and mix thoroughly NORIPET mixture NORIPET 005 activation, life 812 hours, depending on the temperature and humidity conditions. 
 Thinner NoriPET 090 (fast) 
 Slow slow drying agent drying agent NoriPET 097 (middle) 
 Slow drying agent NoriPET 097/001 (very slow) 
 All solvents can be mixed in different ratios to achieve the desired drying rate. 
 Antistatic agents Norilin C, in order to prevent static electricity (especially print metallic case) proposed to add: 0.5% 
 Defoamer according to the actual situation, such as the printing speed and the dilution ratio may need to add defoamers. Add content: 0.20.5% Defoamer 9319 
 Cleaning equipment available screen and thinner NoriPET 097 or Baolong UniREIN A III cleaning. 

 Drying 
 NoriPET by solvent evaporation to dry. Chemical cross-linking process has been carried out, even in the dry rack. 
 Can improve the drying effect of the following ways: 
 Increasing the drying temperature 
 Using the IR drying (starting from the second heating section) 
 The heating channel has evaporated the solvent has drained - good air exchange. 
 When using segmental tunnel ventilation drying, it is recommended: 
 The first paragraph: 80 ° C (175 ° F). 
 Finally, take a thin film of high ventilation to cool to room temperature to prevent the adhesion of thin film stack. 
 The results depend on the diluent gentle drying agent and the dry ink layer thickness and oven efficiency. 


 Final drying 
 To achieve the best heat resistance and durable with the plastic resin bond strength, NoriPET must finally